epoxy ceramic bead repair putty used in repairing and protecting various aluminum casting defect
and aluminum parts wear under the high temperature working condition.
Product description of BD118 high temperature aluminum metal ceramic bead epoxy repair putty compound:
It’s the high temperature high performance polymerization metal materials compounded by various alloy material and
modified toughening heat resistant resin.The highest temperature resistance is 300 degree,suitable for the repairing of
various aluminum casting defect and aluminum parts wear under the high temperature working condition.
The color after repairing is basically the same as the substrates,with the very high strength and excellent wear&corrosion
resistance and aging resistant properties,can do various mechanical processing together with substrates.
How to use of BD118 metal aluminum high temperature resistant repair compound epoxy ceramic putty:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,then clean it by cleaning agent.
2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,
then use it up within specified operation time limit.
3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance
4.Curing: Cure for 2 hours at the temperature of 25-30 degree,heat it up to the temperature of 80 degree and keep this temperature
for 2 hours or it can be put into using after curing for 24 hours at the temperature of 25-30 degree,if the temperature is low,
should heat it up or prolong the curing time to promote the curing.
product index:
| product name | physical state | standard packaging |
volume (cm3) |
operational time limit (25¡æ) |
usable time (25¡æ) |
|
BD118 high temperature aluminum repair agent rebuilding compound |
paste |
250g/set Two-component |
178 | 45min | 24h |
| color |
density (g/cm3) |
compressive strength (kg/cm2) GB1041-2008 |
shear strength (kg/cm2) GB7124-2008 |
bending strength (kg/cm2) GB1042-1999 |
hardness £¨Shore D£© ASTM-D-2556 |
working temperature £¨¡æ£© |
| aluminum | 1.41 | 971 | 149 | 467 | 89 |
-60¡«250 |
Product packaging photo of BD118 high temperature wearing metal aluminum ceramic epoxy compound repair putty: