used in the repairing and protecting of various carbon steel,alloy steel and stainless steel.
Product description of BD112 metal steel epoxy repair putty high temperature abrasion wearing resistant compound:
It’s the high performance polymerization metal materials compounded by various alloy material and modified toughening
heat resistant resin,suitable for the repairing of various carbon steel, alloy steel, stainless steel.Such as fill up casting
defects and repair parts wear,scratch, corrosion, rupture. The color after repairing is basically the same as the substrates,
with the very high strength and excellent wear&corrosion resistance and aging resistant properties,
can do various mechanical processing together with substrates.
How to use of BD112 wearing high temperature resistant compound steel metal
epoxy repair putty:
1.Surface treatment: Do the coarsening treatment on the pending-repair surface and clean it by cleaning agent.
2.Configuration: According to the mass ratio A:B=7:1 or volume ratio A:B=4:1,make A and B two components mix uniformly,
then use it up within specified operation time limit.
3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
If the following working procedure needs machining,should keep out appropriate machining allowance
4.Curing: Curing for 8 hours at the temperature of 25-30 degree before doing machining,It can be put into suing after
curing for 24 hours,if the temperature is low,should heat it up or prolong the curing time to promote the curing.
Performance index:
| product name | physical state | standard packaging |
volume (cm3) |
operation time limit (25¡æ) |
usable time (25¡æ) |
|
BD112 steel metal repair rebuilding compound |
paste |
500g/set Two-component |
298 | 45min | 24h |
| color |
density (g/cm3) |
compressive strength (kg/cm2) GB1041-2008 |
Tensile strength (kg/cm2) GB6329-2008 |
shear strength (kg/cm2) GB7124-2008 |
bending strength (kg/cm2) GB1042-1999 |
hardness £¨Shore D£© ASTM-D-2556 |
working temperature £¨¡æ£© |
| steel | 1.68 | 1064 | 391 | 265 | 582 | 93 |
-60¡«193 |
Product packaging actual picture of BD112 metal steel high temperature wear abrasion resistant epoxy
repair putty compound: