super high temperature wearing repair ceramic epoxy putty

¡¡¡¡BD767 super high temperature anti abrasion wearing resistant epoxy ceramic bead repair agent putty compound
used in the defect filling  and bonding of metal and ceramic under high temperature working condition.

Product description of BD767 wearing resistant super high temperature repair epoxy ceramic bead agent putty compound:

Two-component,inorganic bonding material.the A component is white(or light red) powder(125g),
the B component is translucent liquid(125g) Temperature resistance can reach to 1200 degree.Used in the defect filling 
and bonding of metal and ceramic under high temperature,also used in repairing of high temperature equipment 
like blast furnace lining,metal solution temperature measuring probe and so on,the joint should be designed for 
the socket or mosaic structure during bonding.

How to use of BD767 super high temperature abrasion wear resistant ceramic repair agent epoxy putty:
Mixing weight ratio: 
Can adjust it between A£ºB£½1 : 1.5 and A:B=1.5 : 1 according to the requirements.
Curing condition:
cure at room temperature for 2¡«4 hours,and heat it up to the temperature of 60¡«80 degree and keep this temperature for 2 hours,then heat it up to the temperature of 150 degree and keep this temperature for 2 hours,after that cool it down to the room temperature slowly.
Operation time limit: 20¡«30 minutes.
Note:
Curing strength is low at the room temperature,if there is no heating measures,the curing time at the room temperature 

is at least 5-7 days before using,although in strict accordance with the curing condition,place it for 2¡«4 hours at the room temperature first,then heat up to the temperature of 60¡«80 degree slowly and keep this temperature for 2 hours,after that heat up to the temperature of  150 degree slowly and keep this temperature for 2 hours,then cool it down to the room temperature slowly.If the production rhythm 
is allowed,try to place a long time at the room temperature for heating,it helps to reduce the generation of porosity.
Avoid direct heating or too fast heating speed,the cooling speed can’t also be too fast,had better use furnace cooling.
If the condition is allowed,can separately heat up the A component to remove a small amount of water that 
can absorb before using.

Product packaging photo of BD767 super high temperature resistant epoxy repair agent ceramic bead putty compound:



------·Ö¸ôÏß----------------------------
abrasion wear
resistant coating
crusher backing
compound
anti corrosion
resistant coating
slurry pump
repair coating
industrial ceramic
epoxy adhesive
rubber liquid
coating
thermal heat
insulation coating
skid resistant
coating
heat conduction
coating
thermal conductive
adhesive
high temperature
resistant adhesive
high strength
structural adhesive
industrial repair
agent
rubber metal
bonding adhesive
elastic flexible
adhesive
high temperature
anti seizure compound
high temperature seize
resistant agent
bearing anti wear
fastening adhesive

CEO Email: jimmy@realbond.net        Tel:86-0710-3122805        Fax:86-0710-3618337