wear resistant ceramic adhesiv > powder concentrator repair anti abrasion ceramic adhesives

powder concentrator repair anti abrasion ceramic adhesives

BD133 powder concentrator repair special wear abrasion resistant ceramic epoxy compound adhesives

performance features:
1.It’s the Two-component adhesive consist of modified toughening resin and composite curing agent
2.Water resistant, aging resistant,good toughness, high strength)
3.Can cure at the normal temperature, can also heat up for curing)

product usage:
High bonding strength,good toughness,water resistance excellent,with the high bonding strength for the metal-ceramic bonding,it’s exclusively used in the paste of wear resistant ceramic chip of powder concentrator inner wall.

performance index:

product name	physical state	standard packaging	operation time limit (25℃)	usable time (25℃)	range of application
BD133 powder concentrator wear resistant ceramic adhesive	flow paste	5kg/group	45min	8 hours	Used in the self-adhesion and each-adhesion between metal, ceramic and other materials. Especially used in the paste of wear resistant ceramic tile on the powder concentrator inner wall.

item	color	density (g/cm3)	shear strength (Mpa) GB7124-2008	impact strength (J/cm2) GB6328-1999	tensile strength (Mpa) GB6329-2008	compressive strength) (Mpa) GB1041-2008	working temperature （℃）
BD133	white	1.36	15	51	86	89	-60-150

How to use:
1.Surface treatment: Grinding or sand blasting to clean up the dust,greasy dirt and rust on the inner wall of powder concentrator,
clean it by cleaning agent in the end.

2.Configure adhesive: According to the specified requirements,make A and B two components mix uniformly A:B=4:1

3.Using adhesive: Make configured adhesive spread coating on the surface of adherend uniformly,
under the precondition of no shortage of adhesive,scrape the adhesive layers to be the thinner the better.
Coating adhesive for double sides(powder concentrator inner wall and ceramic side) will get the best effect.
Then make the ceramic chip paste on the powder concentrator inner wall and to be compacted.

4.Curing: Initial curing at the room temperature for 4 hours,fully curing for 24 hours(15MPa),
heat it up to the temperature of 80℃ and keep this temperature for 2 hours,then do the last curing,
in this way,it can get the higher combination property.(can improve 30%). When the temperature is low in winter,
after the completion of the paste,should keep a certain environment temperature to make the adhesive cure fully
(make the adhesive cure at the temperature above 15 degree as far as possible),
can do irradiation heating with iodine tungsten lamp.

5.The configured adhesive should be used up before initial curing.Every time the suitable quantity of
configuring adhesive is 300g～500g,too much adhesive is not easy to mix uniformly,every time the usable time of
configuring adhesive is about 30～40 min,the usable time is long at the low temperature,the usable time is short at
the high temperature,should adjust the configured adhesive quantity according to the actual condition.

Packaging specification:
Packed in a plastic drum, A component: 4Kg/drum, 4 drums/carton; B component: 1Kg/drum,12 drums/carton
or 8 drums/carton.

Transportation storage:
Sealed storage in the cool and dry place. The warranty period is 1 year. Avoid placing it upside down,
knocking against and transporting it as a non-dangerous product during transportation.