The first of Nov,2016,dayudu water-lifting project is a national level large-scale electric pumping station which is built in 70s of th century,it is total
6 grades 10 stations,the total discharge head can reach to 326.8 meters,the one time high lifting of the second grade station is 193.2 meters,it is second
to none in the domestic agricultural irrigation,but as the long operation time,aging and damage are serious,pump casing of main water pump is attenuation,
it has penetrable danger,it has endangered the safety operation of the project,the natural discharge head of the second grade pump station is high,
although the quantity of sediment can reduce by 50%-70% after the yellow river water passing desilting,as the middle embankment and north
embankment desilting pool can not be two-compartment alternant operation,it will affect fast speed sand flushing,it will make the sand content of
outer pool water be larger,
General sand content of each cubic water is about 10Kg,sometimes individual even can reach to 60-70Kg,it will cause
serious damage of water pump casing,impeller,clapboard and baffle tongue,and lead to water pump high and low pressure chamber complicity,
and make most of pump casing be take on cellular status,some of them have more than 15mm deepth,it has penetrable danger,flow resistance
inside of pump will increase,water flow regime will worsen,water pump efficiency will go down,the test result of pump station test centre doing
the sampling test for partial machine set shows that:the pump efficiency is only about 65%,it will affect the normal operation of pump station seriously,
if they don’t solve the abrasion problem,all levels of the pump station can not be stable operation.
Dayudu water-lifting project Debt Management Office passed discuss and filter,they finally decide to use BD7045 pump special abrasion wear resistant
coating of Xiangyang City Hundred Shield to repair clarified water pump abrasion parts,it will effectively increase the service life of pump parts,the
clarified water pump after repairing in the weekly check,if you found that each part of the substrates appears abrasion again,you could use wear
abrasion resistant coating adhesive to do the replenish repairing,reciprocating like this,the working life of pump parts will prolong several times,
the economic benefit is very considerable,in order to prolonging using time of repairing for one time,the customer can not only plug up wear through
holes during repairing,but also smear a layer(coating thickness: 4mm-8mm) of anti wear abrasion resistant coating to do pre-protecting on the whole
pump casing inner wall.